Properties

The coating dries quickly, is hard and   provided with excellent adhesive ability. The coating can be solidified at   low temperature；

With good oil resistance, water resistance,   age resistance, cathodic protection property   and ocean climate resistance;

The rust cycle is 6~7 months;

The coating is heat resistant, capable of long-time service at 400℃(752℉), of with excellent capable of flame cutting and solderability.

The content of lead and heavy metal   all are in accordance with the requirement   of environmental standards in theUnited Statesand Europe.

Designed Applications

Applicable to the temporary protection of   steel structure in offshore installations, chemical plants, petrochemical   plants power stations, bridges   etc.

Color

Grey

Working Parameters

Lustre

Solid volume

Flash point

Drying time（25℃）

Semi-lustrous

35%

13℃(37.4℉)

Surface drying time: 5 mins

Hard drying time: 4 hrs

Coating thickness and theoretical coating   ratio

Actual Coating Ratio         Loss coefficient properly considered

Suggested times of coating

Spraying once, dry coating thickness as 15~20   microns, The   thickest part as no more than 25 microns.

Subsequent coats

Epoxy zinc   phosphate antirust paint, micaceous iron epoxy antirust paint, epoxy   intermediate coat; chlorinated rubber, polyurethane and organic silicate   finish paint.

Surface Treatment

Ø     Be sure to get rid of the oil   stain and weld spatters on the steel plate before rust removal, and burnish   welding seams and closed angles;

Ø     Use sand blasting for surface   treatment: remove oxide skin and iron rust, with the cleanness reaching Sa   2.5 Level, roughness: 40~75 microns. If oxidation appears on the steel   product surface to be coated after sand blasting, this surface should be   treated with sand blasting again until it reaches the specified standard.

Ø     It is not recommended to use   this product on the surface on which rust removed manually.

Temperature of

base material

The temperature of base material must be   over 3℃(37.4℉) above the dew point.

The recommended temperature of base   material is 30~40℃(86~104℉).

Usage

Mixing

The product is packed in two containers   separately that form a unit. For use every time, completely and uniformly mix   it according to the specified compounding ratio; and keep stirring during   spray painting in order to prevent zinc dust precipitation. The product must   be used up within the specified mixture pot life.

Mixing ratio

A:B=1: 1 (volume ratio)

A: B=2: 1 (weight ratio)

Pot life: (after mixture)

Ways of

Coating

Airless spraying, aerial spraying, brush   painting or roller painting

Airless   spraying

Diluting agent

GLX-1 Thinner

Dosage

0~5% (Weight of paint)

Spray nozzle

calibre

about 0.53~0.64mm(0.021~0.025″)

Spraying pressure

14~16MPa(140~160Kg/cm²，2000~2200psi)

Aerial   spraying

Diluting agent

GLX-1 Thinner

Dosage

5~10% (Weight   of paint)

Spray nozzle

calibre

2.0~2.5mm(0.079~0.098″)

Air pressure

0.3~0.6MPa(3~6Kg/cm²，42~85psi)

Brushing paint;

Roller

paint

Only suitable for repair and small-area   coating.

Cleaning agent

GLX-1 Thinner

Safety Protection

There should be good ventilating devices   provided at the work site. During working, wear the appliances for labor   protection such as gauze mask, spectacles, gloves, etc. to avoid skin contact   with and suction of solvent or paint fog. Smoking is forbidden at the work   site, and all fire sources shall be isolated.

Latter

compatible paint

We recommend that this whole paint is used in company with following   products:

If you want to know other kinds of   compatible coating, please consult the  technical services division in Wuhan Gelin Coating   Limited Company. 

Storage and

Packing

Packing

20 kl Group

Ingredient A

20L Pail Pack

10 kl

Ingredient B

10L Pail Pack

10 kl

Storage

25℃（77℉）

6 months (Exceeding the storage life, the   product must be retested, and can be used only if passing the test.)

The product should be kept at cool and   dry place, away from heat sources and fire sources.

Precautions

l           If the temperature is above 30℃（86℉）, 5~10% GLX-1 Thinner should be added to prevent dry spraying   during working.

l           If the dry coating thickness   is below the requirement, recoating with VICHZINC1020   is needed. Before recoating, the VICHZINC1020   should be diluted with 40% GLX-1 Thinner, which is to increase the adhesive   force between the layers of paint film.

Notice

1. The data in   the Description of Product are merely the instruction for use. This company   will provide technical support and on-site service at the user’s request so   as to ensure the normal proceeding of the working. For non-normal coating and   its application, this Company only guarantees the technical indicators of the   products.    